Product Description
T
NA1005
NA Jointing Sheet
Desciption and Applications
TEADIT style NA1005 is a compressed non-asbestos jointing-sheet material produced from Aramid fibres, bonded with Nitrile Rubber (NBR). It is being manufactured by means of a hot calender process under rigorous quality control standards which are registered under ISO 9001 certification.
Please note: the colour of the actual product might vary from the above image on this data-sheet.
Style NA1005 is indicated for air, brine, water, low pressure steam, organic and weak inorganic acids, diluted and concentrated alkalis, petroleum derivatives, synthetic and vegetable oils, aliphatic and chlorinated solvents, refrigerants, gases and chemical products in general.
Approvals
- Germanischer Lloyd
- KTW
- ABS Certificate
Service Limits
| Temperature (ºC) | Continuous Service: 240 |
| Maximum Service: 400 | |
| Pressure (bar) | Continuous Service: 50 |
| Maximum Service: 110 |
| Availability (in mm) | 1.500 x 1.600 |
| 1.500 x 3.200 | |
| Thickness (in mm) | 0.5/1.0/1.5/2.0/2.5 and 3.0 |
| Color | Green |
| Typical Physical Properties: | ||
|---|---|---|
| Density | app. 1,75 g/cm3 | |
| Compressibility - F36 | 7-17% | |
| Recovery - ASTM F36 | 45% | |
| Tensile Strength, Transverse - F152 | 11,5 N/mm2 | |
| Residual Stress - DIN 52913 | 28 N/mm2 | |
| Creep Relaxation - F38 | 25% | |
| Sealability at 1000 psi - F37 A | 0,25 ml/h | |
| Thickness Increase - ASTM F146 - after 5hr | ||
| ASTM Oil Nr.3 @ 150ºC | 12% | |
| Fuel B, @ +21-29ºC | 10% | |
| Weight Increase - ASTM F146 - after 5hr | ||
| ASTM Oil Nr.3 @ 150ºC | 15% | |
| Fuel B, @ 21-29ºC | 15% | |